论文标题
$ j_ \ textrm {eff} = 1/2 $kagomé系统SM $ _3 $ _3 $ sb $ _3 $ zn $ _2 $ _2 $ o $ _ {14} $
Magnetic transition in the $J_\textrm{eff} = 1/2$ Kagomé system Sm$_3$Sb$_3$Zn$_2$O$_{14}$
论文作者
论文摘要
我们介绍了SM $ _3 $ SB $ _3 $ Zn $ _2 $ o $ o $ _ {14} $（SSZO）的研究，该研究通过磁化和特定的热容量$ C_P（T）$测量值。 SSZO包含sm $^{3+} $磁离子的良好平面。尽管我们的磁化率（数据限制为2 \，k）没有显示任何异常，但已将$ c_p（t）$数据显示为0.35 k，在$ t \ sim1.5 $ \，k时显示出广泛的最大值，k，k，随后是$ t \ sim0.5 $ \，k，k，k，k，k，k，k，k，k表示短距离和远程范围。
We present a study of Sm$_3$Sb$_3$Zn$_2$O$_{14}$ (SSZO) through magnetization and specific heat capacity $C_p(T)$ measurements. SSZO contains well separated planes of Sm$^{3+}$ magnetic ions on a Kagomé lattice. Though our magnetic susceptibility (where the data are limited down to 2\,K) does not show any anomaly, the $C_p(T)$ data which have been taken down to 0.35 K reveal a broad maximum at $T\sim1.5$\,K followed by a sharp peak at $T\sim0.5$\,K indicative of short-range correlations and long-range order, respectively.